High Temperature Constructional Steels Bars (DIN 17155, DIN 17175, DIN 17200, SEW 550)

High Temperature Constructional Steels Bars (DIN 17155, DIN 17175, DIN 17200, SEW 550)

Steel Grade				Chemical composition in % by wt (ladle analysis)
DIN		AISI No SAE No	JIS	C	Si	Mn	≤P	≤S	Cr	Mo	Ni	Other Elements
Code Number	Material Number
CK 35	1.1181	1033	S38C	0.32—0.39	≤0.40	0.50—0.80	0.035	0.035	—	—	—	—
CK 45	1.1191	1042	S45C	0.42—0.50	≤0.40	0.50—0.80	0.035	0.030	—	—	—	—
21Mo V 53	1.5404	—	—	0.17—0.25	0.15—0.35	0.50—0.80	0.035	0.035	0.20—0.40	0.45—0.55	≤0.30	V:0.25—0.35
17 Mo V 84	1.5406	—	—	0.14—0.22	0.15—0.35	0.50—0.80	0.035	0.035	0.20—0.40	0.80—1.00	≤0.30	V:0.30—0.40
15 Mo 3	1.5415	—	—	0.12—0.20	0.10—0.35	0.40—0.90	0.030	0.030	=< 0.25	0.25—0.35	—	Cu: ≤0.30
22 Mo	1.5419	4419	SCPH 11	0.18—0.25	0.20—0.40	0.40—0.70	0.035	0.035	=< 0.30	0.30—0.40	—	—
28NiCrMo4	1.6513	—	—	0.24—0.34	0.15—0.40	0.30—0.60	0.035	0.035	1.00—1.30	0.20—0.30	1.00—1.30	—
16 Cr Mo 4	1.7242	—	—	0.13—0.20	0.15—0.35	0.50—0.80	0.035	0.035	0.90—1.20	0.20—0.30	≤0.40	—
24 Cr Mo 5	1.7258	—	SCM 24	0.20—0.28	≤0.40	0.50—0.80	0.035	0.035	0.90—1.20	0.20—0.35	≤0.60	—
13 Cr Mo 44	1.7335	—	—	0.08—0.18	0.10—0.35	0.40—1.00	0.035	0.030	0.70—1.10	0.40—0.60	—	Al≤0.07
16 Cr Mo 44	1.7337	—	—	0.13—0.20	0.15—0.35	0.50—0.80	0.035	0.035	0.90—1.20	0.40—0.50	≤0.40	—
10 Cr Mo 9 10	1.7380	—	SCM 32	0.08—0.15	=< 0.50	0.40—0.70	0.040	0.040	2.00—2.50	0.90—1.20	—	—
14 Mo V 63	1.7715	—	—	0.10—0.18	0.10—0.35	0.40—0.70	0.030	0.035	0.30—0.60	0.50—0.70	—	V:0.22—0.32
24 Cr Mo V 55	1.7733	—	—	0.20—0.28	0.15—0.35	0.30—0.60	0.035	0.035	1.20—1.50	0.50—0.60	≤0.60	V:0.15—0.25
21 Cr Mo V 5 11	1.8070	—	—	0.17—0.25	0.30—0.60	0.30—0.60	0.035	0.035	1.20—1.50	1.00—1.20	≤0.60	V:0.25—0.35

 

  Sizes: Cold Drawn Bars:Dia.2-18mm ; Hot Rolled Bars: Dia. 13-360mm; Forged Bars: Dia.200-1500mm 