monocrystalline silicon solar cells
Efficiency (%) | Pmpp (W) | Umpp (V) | Lmpp (A) | Uoc (V) | Lsc (A) | FF (%) | Type (mono) | |||
17.75-18.00 | 2.77 | 0.527 | 5.245 | 0.631 | 5.591 | 78.42 | Solar cell | |||
17.50-17.75 | 2.73 | 0.524 | 5.213 | 0.628 | 5.566 | 78.17 | Solar cell | |||
17.25-17.50 | 2.69 | 0.520 | 5.177 | 0.625 | 5.536 | 77.85 | Solar cell | |||
17.00-17.25 | 2.65 | 0.515 | 5.152 | 0.623 | 5.564 | 76.72 | Solar cell | |||
16.75-17.00 | 2.61 | 0.510 | 5.121 | 0.624 | 5.563 | 75.33 | Solar cell | |||
16.50-16.75 | 2.57 | 0.504 | 5.107 | 0.622 | 5.575 | 74.25 | Solar cell | |||
16.25-16.50 | 2.54 | 0.505 | 5.038 | 0.625 | 5.579 | 72.94 | Solar cell | |||
*RATIO OF VOC(LSC) AT REDUCED INTENSITY TO VOC(LSC) AT 1000M2 | ||||||||||
MECHANICAL DATA AND DESIGN | INTENSITY DEPENDENCE | |||||||||
Dimensions 125*125±0.5(mm) | Intensity [W/M2] | Lsc*[MA] | Voc*([MV] | |||||||
Thickness 180±20(um) | 1000 | 1.0 | 1.000 | |||||||
Front (-) 1.9mm bus bars(silver) ,blue anti-reflecting coating (silicon nitnde) | 900 | 0.9 | 0.989 | |||||||
500 | 0.5 | 0.963 | ||||||||
Back (+) 3mm wide soldening pads(silver) back surface field (aluminium) | 300 | 0.3 | 0.939 | |||||||
200 | 0.2 | 0.920 | ||||||||
TEMPERATURE COEFFICIENTS | ||||||||||
Tkvoltage : -0.356%/k Tkcurrent :+0.024%/k Tkpower: -0.46%/k | ||||||||||
Remark: The dimensions above are just for your reference, the final figures are subject to our final confirmation. | ||||||||||
Mono crystalline silicon solar cell