Introduction of Liquid Silicone for Plaster Moldmaking
Liquid Silicone for Plaster Moldmaking is a kind of two-component material, that is the moldmaking silicone rubber is made up of Part A base silicone and Part B CA30 curing agent. The mixed Part A base silicone and Part B curing agent can cure at room temperature by a condensation reaction,and the become a siliconer rubber mold that can be used for objects reproduction.These RTV-2 silicone rubber molds can be cast into different material for your target objects.The pouring material can be plaster, polyurethane, PU, GRC, cement, resin, polyester, wax etc...
Characteristics of Liquid Silicone for Plaster Moldmaking
1. Good flow ability and long working time
2. Medium hardness
3. High tear and tensile strength
4. Easy de-mould from complex replica parts
5. Acid and alkali-resistance
6. Low linear shrinkage
Applications of Liquid Silicone for Gypsum Moulding
Liquid Silicone for Plaster Moldmaking is suitable for the reproduction of cement molding, concrete stones, artificial stones, plaster molding, figures, art objects, decoration molding, GRC products, gypsum products, resin products, PU molds. Etc.
Instructions for Making Silicone Moulds
1. Make sure the surface of the original is clean and free of loose material.
2. Weight 100 Part A base and 2 parts of CA30 Curing Agent in a clean container.
3. Stir Part A base silicone before use thoroughly , as filler separation may occur upon prolonged storage.
4. Mix Part A and Part B evenly until the CA30 completely dispersed in the base.
5. Pour the mixed Part A base silicone and CA-30 curing agent as soon as possible onto the original
6. De-mold after 24 hours ,it is will improve the replicate times of silicone mold.
Note:It is strongly recommended that entrapped air be removed in a vacuum chamber, allowing the mix to completely expand and then collapse. After a further 1-2 mins under vacuum, the mix should be inspected and can be used if free of air bubbles. A volume increase of 3-5 times will occur on vacuum de-airing the mixture. So a suitably large container should be chosen.
Shortage of Liquid Silicone for Plaster Moldmaking
When the Liquid Silicone for Plaster Moldmaking is stored at or below 30 °C(85 °F) in the original unopened containers, RTV2 Silicone Base and CA30 Curing agent have a usable life of 10 months from the date of production. After 10 months, please use a stockpile to stir the Part A silicone for some minutes, then the silicone can be use again, no influence for other performance.
The information above is just for reference, if you're interested or have any questions, please feel free to contact Nicole:
Tel: 86-15874272919
Web:www(dot)mcsilicone(dot)com
E-mail:nicole(at)mcsilicone(dot)com
Skype:nicoleszmc
MSN: nicoleszmc (at)hotmail(dot)com