It has excellent heat resistance, improved processing performance,good fluidity and bonding characteristic.

Items	26404	26504
Appearance	white or light-yellow film	white or light-yellow film
Density	1.82±0.02	1.82±0.02
Moner viscosity	45±5	55±5
Fluorine content	66	66
Tensile strength after press cure(Mpa)177°C,10min≥	9.0	9.0
Tensile strength after post cure(Mpa)230°C,24H≥	13.0	13.0
Elongation at break after post cure(%) 177°C,10min≥	180	180
Elongation at break after post cure(%) 230°C,24H≥	160	160
200°C,inNO.3 jet fuel, weight increase after 24H(%)≤	5	5
water content(%) ≤	0.15	0.15
200°C,70Hcompressibility 20%compression set (%)≤	20	20

Typical application:"O"ring,oil seal,calendering sheet and complex structural rubber units, etc

Wide molecular weight distribution series fluoroelastomer