Safty shoes and Army boots

Characteristic: high strength and cohesive force, good abrasion resistance and skid resistance

Application: Double density sole system for common safety shoes and one-step forming casual shoes

Typical properties of PU matrix

 Materials preheat

A-6180         preheated at 50~60°C for 16~18 hours          

B-6280         preheated at 50~60°C for 18~20 hours

Typical processing parameters & Reaction parameter

  The adding content of C-2 should be 300g±20g/18kg polyol

  The adding content of water and hardener should be changed according to the reality

Out sole      H2O 20~30g/18kg         Hardener 0~400g/18kg polyol               

mid-sole     H2O 50~55g/18kg        Hardener 0~600g/18kg  polyol     

Physical properties

Demold time may be prolonged with the increase of sole thickness

These physical data are acquired by testing a sample of 6mm thick.

Data listed above are just for reference.