The first ETFE Powdermanufacturer
in China--Jiangsu Huaao High-Tech Development Co., Ltd., which is supply products to DuPont in large quantity throughout the year.
HAFZEL ETFE GDES
Item Name | Thickness | Application | process method |
P-8820 | 50~80µ | non-stick cookware | Powder coating |
P-885A | 50~150µ | non-stick coiled material | Powder coating |
50~400µ | anti-corrosion machine | Dipping coating | |
RL-522 | 2~5mm | reactor,pump,tank | Rotomolding |
RL-581 | 2~5mm | Rotomolding |
PHYSICAL PROPERTY
Testing | Unit | P-8820 | P-885A | RL-522 | RL-581 |
Melt flow speed | g/10min | 10~15 | 10~15 | 9~12 | 20~30 |
Proportion | - | 1.70~1.74 | 1.70~1.74 | 1.70~1.74 | 1.70~1.74 |
Melting point | °C | 260~270 | 260~270 | 260~270 | 260~270 |
tensile strength | Mpa≥ | 30 | 30 | 30 | 30 |
tensile elongation | %≥ | 300 | 300 | 300 | 300 |
modulus of flexible | Mpa | 960 | 930 | 910 | 890 |
strength of flexible | Mpa | 26 | 25 | 25 | 25 |
impact strength | J/m | No break | No break | No break | No break |
liner thermal expansion | 10-5/°C | 9.3 | 9.3 | 9.4 | 9.4 |
oxygen index | % | 32 | 32 | 32 | 32 |
thermo chemical resistance | - | Good | 2.6 | 2.6 | 2.6 |
Permittivity(102-106Hz) | - | 2.6 | 2.6 | 2.6 | 2.6 |
molding shrinkage | % | 1.8 | 1.8 | 1.8 | 1.8 |