Ningbo Eagle New Material Co., Ltd
Model NO. – HG1030C Color – Black
Properties | ASTM | Units | Actual Test Date | |
Mechanical Properties | ||||
Tensile Strength | D638 | MPa | 124 | |
Tensile Modulus | MPa | / | ||
Elongation at Break | % | 4 | ||
Bending Strength | D790 | MPa | 156 | |
Bending Modulus | MPa | 6600 | ||
IZOD Impact Strength | 1/4 | D256 | KJ/m2 | 6.5 |
1/8 | 7.2 | |||
Thermal properties | ||||
Melting Point | D | °C | / | |
Heat Deflection Temperature(1.82Mpa) | D648 | °C | 150 | |
Melting Index | D1238 | g/10min | 100 | |
Flame Resistance Properties | UL94 | HB | HB | |
Physical Properties | ||||
Density | D792 | g/cm3 | 1.38 | |
Ash Content | ISO3451 | % | 30±2 | |
Water Absorption (24H/23°C) | D570 | % | / | |
Molding Reduction | D955 | 10-3mm/mm | / | |
Electrical Properties | ||||
Dielectric Strength | IEC 60243-1 | KV/mm | / | |
Volume Resistivity | IEC 60093 | Ω·m | / | |
Surface Resistivity | IEC 60093 | Ω | / | |
Remark Molding Reduction test size: 129×12.7×3.2mm.This is a typical property report, just for reference only. | Experimental Condition: ¹ Temperature:23°C ² Relative Humidity (RH): 60% | |||
Description: 1. Good heat resistance
2. High rigidity
3. Good stability
4. High liquidity
Dry and injection molding process:
Drying time: 80-90 °C / 2 hours
Injection temperature: 250-270 °C
Moulding temperature: 80-100 °C
reinforced PA6 with 30% GF black