Shrinkable Temperature ( °C )

>= 200

Concentricity (%)

>= 60

Radial Shrink Range (%)

>=  45

Ultimate Elongation Ratio

300

Operate Temperature Range

-80 °C ~280 °C

Coefficient of Dynamic Friction

0.1

Longitudinal Change (%)

<= 10

Specific Gravity (g/cm 3 )

2.16

Aging in Circulating-air Oven

300 °C

Tensile Strength (MPa)

20.5

Aged Tensile Strength Break Elongation

20 200

Impact Strength

-No Break -107

Volume Resistivity ( Ω. cm)

>10

Flexural Modulus (MPa)

400

Breakdown Strength (KV/mm)

30

Hardness (Shore D)

85

Flammability

VW-1

Softening Point ( °C )

350

Operate Temperature ( °C )

-280~300

Flammability

VW-1

Dissipation Factor

0.0002

Weather Resistance

No Break

Dielectric Constant

2.1

Original Volume Resistivity ( Ω. cm)

1018

Arc Resistance

300

Solvent Resistance

Excellent

Chemical Resistance

Excellent

Size

Before Shrink

After Shrank

I.D. (mm)

Average Layer

Thickness (mm)

I.D. (mm)

Average Layer

Thickness (mm)

Average Layer Thickness (super thin)  (mm)

Φ0.5

0.5±0.2

0.15±0.1

≤0.30

0.20±0.1

0.10±0.05

Φ0.8

0.8±0.2

0.15±0.1

≤0.35

0.20±0.1

0.10±0.05

Φ1.0

1.0±0.2

0.15±0.1

≤0.50

0.20±0.1

0.10±0.05

Φ1.5

1.5±0.2

0.20±0.1

≤0.75

0.25±0.1

0.10±0.05