Impregnation Adhesives for Carbon Fibre 1.Modified epoxy resin 2.Good penetration 3.Low viscosity 4.Water resistance

HM-180C3P Modified Epoxy Resin Carbon Fiber Impregnation Adhesive is used for impregnation and paste of reinforced component surface and fiber products.

It is completely impregnated in fiber products, and coheres fiber products effectively with the component surface, thereby to strengthen the components.

1. Product Characteristics

1) Good compatibility with carbon fiber.

2) Aging, water resistance and chemical corrosion resistance, excellent performance.

3) Low viscosity, can completely impregnated in fiber products.

4) The adhesive layer has excellent physical mechanical properties after curing, such as strong toughness and elasticity.

2. Application Range

This product is epoxy fiber adhesive of high performance, which is mainly used for the strengthening and reinforcement of buildings.

It can be used for the effective penetration bonding between many substrate materials and many fiber fabrics.

Substrates can be concrete, steel material, ceramic, stone, wood component, etc.

Fiber products can be carbon fiber, glass fiber, basalt fiber, aramid fiber, etc.

3. Working Performance

Slump (40°C)	2.0 mm
Operable Time (40°C)	> 60 min
Applicable Temperature	5 ~ 40 °C

4. Colloidal Performance

Compressive Strength	≥ 70.0 MPa
Tensile Strength	≥ 40.0 MPa
Bending Strength	≥ 50.0 MPa
Elastic Strength	≥ 2500 MPa

5. Bonding Capacity

Steel–steel Tensile Shear Strength	≥ 14 MPa
Pulling Bonding Strength along with Concrete	≥ 2.5 MPa

6. Usage Amount

The usage amount is 0.6-0.9 kg for a square meter of fiber cloth.

7. Package

30 kilograms per set. A net: 20 kilograms (Nor.) B net: 10 kilograms (Nor.)Other packing weight is optional according to customer's requests.