Senke exports ultra-fine stainless steel wire and wire diameter from 0.018mm to 0.25mm.Fine wire from 0.20 to 5mm.
Stainless Steel Wire
Material | Condition | Tensile Strength (MPA) | Elongation(%) |
304 Tensile Strength | Cold Drawn Wire | 1000 -1200 | 0 |
Annealling Wire | 580 - 680 | 25 | |
Spring Wire | 1500- 1900 | 0 | |
302 Tensile Strength | Cold Drawn Wire | 1000 - 1200 | 25 |
Annealling Wire | 580 - 680 | 25 | |
Spring Wire | 1500 - 1900 | 0 | |
301 Tensile Strength | Cold Drawn Wire | 1000 - 1200 | 0 |
Annealling Wire | 580- 680 | 20 | |
Spring Wire | 1500- 1900 | 0 | |
202 Tensile Strength | Cold Drawn Wire | 1000 - 1200 | 0 |
Annealling Wire | 700 - 900 | 0 | |
Spring Wire | 1500 - 1900 | 0 | |
201 Tensile Strength | Cold Drawn Wire | 1000 - 1200 | 0 |
Annealling Wire | 580 - 680 | 20 | |
Spring Wire | 1500 - 1900 | 0 | |
431 Tensile Strength | Cold Drawn Wire | 790 - 1000 | 0 |
Annealling Wire | 580 - 680 | 30 | |
Spring Wire | 1500 - 1900 | 0 | |
430 Tensile Strength | Cold Drawn Wire | 600 - 800 | 0 |
Annealling Wire | 460 - 640 | 0 | |
410 Tensile Strength | Cold Drawn Wire | 560 - 780 | 0 |
No Magnetic,No Nickel | Cold Drawn Wire | 600 - 800 | 0 |
Annealling Wire | 490 - 680 | 0 |
| Stainless Steel Wire | ||||||||
| AISI Grade | Chemical Composition(%) | |||||||
| C | Si | Mn | P | S | Ni | Cr | Mo | |
| 304 | =<0.08 | =<1.00 | =<2.00 | =<0.045 | =<0.030 | 8.00~10.50 | 18.00~20.00 | - |
| 304H | > 0.08 | =<1.00 | =<2.00 | =<0.045 | =<0.030 | 8.00~10.50 | 18.00~20.00 | - |
| 304L | =<0.030 | =<1.00 | =<2.00 | =<0.045 | =<0.030 | 9.00~13.50 | 18.00~20.00 | - |
| 316 | =<0.045 | =<1.00 | =<2.00 | =<0.045 | =<0.030 | 10.00~14.00 | 10.00~18.00 | 2.00~3.00 |
| 316L | =<0.030 | =<1.00 | =<2.00 | =<0.045 | =<0.030 | 12.00~15.00 | 16.00~18.00 | 2.00~3.00 |
| 430 | =<0.12 | =<0.75 | =<1.00 | =<0.040 | =<0.030 | =<0.60 | 16.00~18.00 | - |
| 430A | =<0.06 | =<0.50 | =<0.50 | =<0.030 | =<0.50 | =<0.25 | 14.00~17.00 | - |
| 321 | =< 0.12 | =<1.00 | =<2.00 | =<0.035 | =<0.030 | 8.00~11.00 | 17.00~19.00 | - |