virgin hdpe granules/Virgin & Recycled hdpe/hdpe resin Advanced equipment Precise granulating High producing capacity
virgin hdpe granules/Virgin & Recycled hdpe/ hdpe resin
Specifications1. Virgin & Recycled 2. Type: Film grade, Injection molding grade, Blowing molding grade, extrusion grade, 3. Pack: 25kg/bag
Virgin & Recycled HDPE / LDPE / LLDPE granules
1. we are direct factory, different MFR or MFI are available for your different usage.
2. good quality and reasonable price
3. non-poteonods no smell adurless
4. it can replaced original plastic material, sometimes it can replace new material
HDPE:
HDPE cable materialProperty | Unit | Typical Value |
Mass density | g/cm 3 | 0.941-0.959 |
Melt flow Rate(190 centidegree /2.16kg) | g/10min | ≤1.0 |
Tensile yield strength | MPa | ≥19.0 |
Flexural modulus | Mpa | ≥965 |
Elongation@ break | % | ≥400 |
Impact Embrittlement temperature | centidegree | MAX -118 |
Dielectric Constant | 100KHZ | 2.32 |
1MHZ | 2.31 | |
Loss Tangent | 100KHZ | MAX 0.0001 |
1MHZ | MAX 0.0001 | |
Volume resistivity | OHM-CM | MIN 1x10 15 |
Application | Mainly used for the production of high toughness of the telephone,cable insulation material | |
LDPE:
Physical Properties | Test Method | Nominal Value | Unit | |
Density | ISO 1183 | 0.921 | g/cm3 | |
Melt Mass-Flow Rate (MFR) | ISO 1133 | 1.9 | g/10min | |
Hardness | ||||
Shore Hardness (shore D) | ISO 868 | 45 | ||
Mechanical Properties | ||||
Tensile Modulus | ISO 527-2 | 175 | MPa | |
Tensile Strength | Yield, | ISO 527-2 | 9.0 | MPa |
Break, | 13.0 | MPa | ||
Tensile Strain(Break) | ISO 527-2 | 850 | % | |
Modulus of Elasticity | Internal Method | 250 | MPa | |
Thermal | ||||
Vicat Softening Temperature | ISO 306/A50 | 89.0 | °C | |
Melting Temperature (DSC) | DIN 53765 | 108 | °C | |
Peak Crystallization Temperature (DSC) | DIN 53765 | 97.0 | °C | |
Heat of Fusion | DIN 53765 | 110 | J/g | |
Electrical | ||||
Volume Resistivity | ASTM D257 | 8.5E+15 | ohm •cm | |
Dielectric Strength | ASTM D149 | 30.0 | kV/mm | |
Dielectric Constant (60Hz) | ASTM D150 | 2.20 | % | |
Dissipation Factor (60 Hz) | ASTM D150 | 0.00050 | ||
LLDPE
Properties | Test conditon | Test method | Test data | Unit |
Density | 0.91 | |||
MFI | 2 | |||
Drop impact strength | ASTM D-1709 | 90 | g | |
Elongation ,vertical/horizontal | ASTM D-882 | 600/800 | % | |
tensilestrength,thermal resistance | ASTM D-1004 | 105/95 | Kg/cm | |
elongation | ASTM D-638 | 930 | % | |
tensile strength | ASTM D-638 | 180 | ||
tensile strength,vertical/horizontal | ASTM D-882 | 380/350 | ||
Vicat softening point | ASTM D-1525 | 103 | °C | |
melting point | ASTM D-2117 | 126 | °C | |
Turbidity | ASTM D-1009 | 12 | % | |
45 glossness | ASTM D-2457 | 75 | % | |