DUAL WALL, ADHESIVE-LINED POLYOLEFIN TUBING
SHRINK RATIO 3:1
Features/Applications
H-5(3000) is manufactured by co-extrusion of polyolefin and
Hot melt adhesive. Designed to provide both insulation and
sealing for electronic components , wire splices cables and
jackets.
Property | Test Method | Typical Data |
Tensile strength | ASTM D 2671 | 12MPa(min) |
Tensile strength after ageing 136°C, 168hrs | ASTM D 2671 | Remains 70% |
Elongation at break | ASTM D 2671 | 400%(min) |
Elongation at break after ageing 158°C,168hrs | ASTM D 2671 | 100%(min) |
Longitudinal shrinkage | UL224 | 0 to -10% |
Heat shock Tensile strength Ultimate elongation | 200°C,4hrs | No cracking, no dropping 270%(min) |
Cold bend -40°C,1hr | ASTM D 2671 | No cracking |
Voltage withstand AC 2500V, 60seconds | ASTM D 2671 | No breakdown |
Volume resistance | ASTM D 876 | 1014Ω.cm(min.) |
Flammability | SAE-AMS-DTL-23053/5 | Self-extinguish in 30 sec. |
Copper corrosion(158°C,168hrs.) | SATM D 2671 | Pass |
Water absorption | ASTM D 570 | <0.5% |
Fluid resistance | MIL-DTL-23053/4 | Good |